Effect of Coating Structure on Powdering Resistance of Galvannealed Steel Sheet NKK Corporation

Format:

Conference/Event

Author/Creator:

Sakurai, Michitaka, author.

Conference Name:

International Congress & Exposition (1992-02-24 : Detroit, Michigan, United States)

Language:

English

Physical Description:

1 online resource

Place of Publication:

Warrendale, PA SAE International 1992

Summary:

AbstractGalvannealed steel sheets containing 10wt%Fe in coated layer were prepared in various galvannealing temperature and cooling rate. Powdering resistances were evaluated by a draw bead test. X-ray diffraction examination revealed an attribution of the coating structure to powdering resistance.Higher galvannealing temperature(500550°C) deteriorates powdering resistance, but slower cooling from higher temperature improves it. At low galvannealing temperature(440°C), powdering resistance is rather good independent of cooling rate. Г1-phase(Fe5Zn21) is formed along the interface between coating and steel when samples are galvannealed at lower temperature(500°C) or cooled at slower cooling rate from higher galvannealing temperature. The results suggest that the increase of Г1 ratio [Г1/(Г+Г1)] in the coating is inclined to improve powdering resistance

Notes:

Vendor supplied data

Publisher Number:

920174

Access Restriction:

Restricted for use by site license