Tribological Factors Affecting the LDH Test University of Waterloo

Format:

Conference/Event

Author/Creator:

Fischer, R.F., author.

Conference Name:

International Congress & Exposition (1992-02-24 : Detroit, Michigan, United States)

Language:

English

Physical Description:

1 online resource

Place of Publication:

Warrendale, PA SAE International 1992

Summary:

The present work is aimed at investigating the tribological factors influencing the LDH test. The material used was AKDQ cold-rolled bare steel, 0.82mm thick. The investigated factors included: test speed (0.833, 4.167, 6.667, and 8.333 mm/s), lubricant viscosity (4.5, 7.0, and 12.5 mm2/s), punch roughness (0.033 and 0.144 μm Ra), and test temperature (25 and 50 °C). Test speed and lubricant viscosity form a variation of the numerator of the Stribeck curve's x-axis (ηV). With ηV increasing from 4 to 120 mm3/s2 friction decreased, resulting in a 0.5 mm higher LDH. Increasing the punch roughness decreased friction producing an increase of 0.25 mm in the LDH. There appears to be an optimum roughness -- at which the roughness features act as lubricant reservoirs but the asperities do not break through the lubricant film -- resulting in minimum friction, therefore, maximum LDH. Beyond the effect test temperature has on the lubricant (which was accounted for in the lubricant viscosity), test temperature affected the material's formability: increasing the test temperature reduced the LDH by approximately 1.00 mm. The reasons for this effect are not known at present time

Notes:

Vendor supplied data

Publisher Number:

920434

Access Restriction:

Restricted for use by site license