Fabrication and Mechanical Properties of Alumina Nanoparticle Reinforced Magnesium Metal Matrix Composite by Stir Casting Method PRIST
- Format:
- Conference/Event
- Author/Creator:
- T. T., author.
- Conference Name:
- International Conference on Advances in Design, Materials, Manufacturing and Surface Engineering for Mobility (2018-07-20 : Chennai, India)
- Language:
- English
- Physical Description:
- 1 online resource
- Place of Publication:
- Warrendale, PA SAE International 2018
- Summary:
- AbstractIn the present experimental investigation magnesium based alloy was prepared by mixing magnesium powder and aluminium powder in the ratio 65:35. The prepared magnesium alloy is used as the matrix material. Metal matrix composites were prepared by stir casting route. The composite was prepared by reinforcing 50 nm alumina nanoparticle so that the final composite contains 5, 10 and 15 wt.% alumina. Mechanical properties such as tensile strength, yield strength, impact strength and hardness were evaluated. Significant improvement was observed in impact strength and hardness value. The result showed that magnesium alloy with 5 wt.% alumina nanoparticle has a maximum impact strength of 25.2 J and hardness value 63.86 Hv respectively. Tensile strength and yield strength shows marginal increase in value
- Notes:
- Vendor supplied data
- Publisher Number:
- 2018-28-0098
- Access Restriction:
- Restricted for use by site license
The Penn Libraries is committed to describing library materials using current, accurate, and responsible language. If you discover outdated or inaccurate language, please fill out this feedback form to report it and suggest alternative language.