Modeling Fracture in Laminated Automotive Glazing Impacted by Spherical Featureless Headform University of Missouri-Rolla

Format:

Conference/Event

Author/Creator:

Dharani, L. R., author.

Conference Name:

SAE 2003 World Congress & Exhibition (2003-03-03 : Detroit, Michigan, United States)

Language:

English

Physical Description:

1 online resource

Place of Publication:

Warrendale, PA SAE International 2003

Summary:

Laminated glass consisting of two soda lime glass plies adhered by a polyvinyl butyral interlayer (PVB) is used for automotive glazing. This paper describes the application of a dynamic, nonlinear finite element method to investigate the failure modes of a laminated glass subjected to low-velocity impact with a spherical headform. Crack type, crack location and crack initiation time are evaluated using the maximum principal stress and J-integral criterion. Failure occurred due to flexural stresses and not bearing stresses. The first crack always initiated at the center of the outer impacted ply and PVB interface, and later on the exterior surface of the inner ply. The PVB thickness and velocity of impact had little or no effect on the first crack initiation

Notes:

Vendor supplied data

Publisher Number:

2003-01-1225

Access Restriction:

Restricted for use by site license