Response to Hydrogen Charging in High Strength Automotive Sheet Steel Products Colorado School of Mines

Format:

Conference/Event

Author/Creator:

Hilditch, T. B., author.

Conference Name:

SAE 2003 World Congress & Exhibition (2003-03-03 : Detroit, Michigan, United States)

Language:

English

Physical Description:

1 online resource

Place of Publication:

Warrendale, PA SAE International 2003

Summary:

The influences of laboratory-induced hydrogen on the tensile deformation and fracture behavior of selected sheet steels including conventional DQSK and HSLA steels as well as newer DP and TRIP grades were evaluated. The effects of cold work, simulated paint baking, and natural aging were considered. Hydrogen effects were observable by increased flow stress, decreased ductility, altered neck geometry, and altered fracture mechanisms. Differences among the steels and conditions were observed and interpreted on the basis of microstructure, fracture behavior, and theories of hydrogen embrittlement

Notes:

Vendor supplied data

Publisher Number:

2003-01-0525

Access Restriction:

Restricted for use by site license