The role of raw material ingredients of brake linings on the formation of transfer film and friction characteristics Department of Materials Science and Engineering, Korea University

Format:

Conference/Event

Author/Creator:

Cho, Min Hyung, author.

Conference Name:

19th Annual Brake Colloquium And Exhibition (2001-10-28 : New Orleans, Louisiana, United States)

Language:

English

Physical Description:

1 online resource

Place of Publication:

Warrendale, PA SAE International 2001

Summary:

An NAO friction material (low-steel type) containing 15 ingredients was investigated to study the role of transfer film on the coefficient of friction, friction oscillation, and fade resistance. The friction material specimens containing extra 100% of each ingredient were tested using a pad-on-disk type tribotester. A non-destructive method of measuring the transfer film was developed by considering the electrical resistance of the transfer film. Results showed that solid lubricants and iron powder assisted transfer film formation on the rotor surface and abrasive ingredients tended to remove the film. No apparent relationship between transfer film thickness and the average friction coefficient was found in this experiment. Fade resistance was also found to be independent of the transfer film thickness when the stable film was formed on the rotor surface at elevated temperatures. On the other hand, the transfer film on the rotor surface reduced the amplitude of friction oscillation

Notes:

Vendor supplied data

Publisher Number:

2001-01-3130

Access Restriction:

Restricted for use by site license