A New Methodology to Characterize the Influence of Paint Baking and Pre-Straining on the Tensile Properties of Third Generation Advanced High Strength Steels University of Waterloo
- Format:
- Book
- Conference/Event
- Author/Creator:
- Northcote, Rhys, author.
- Conference Name:
- WCX SAE World Congress Experience (2025-04-08 : Detroit, Michigan, United States)
- Language:
- English
- Physical Description:
- 1 online resource cm
- Place of Publication:
- Warrendale, PA SAE International 2025
- Summary:
- The current ASTM A653 standard for determining the bake hardening index (BHI) of sheet metals can lead to premature fracture at the transition radius of the tensile specimen in high strength steel grades. In this study, a new test procedure to characterize the BHI was developed and applied to 980 and 1180 MPa third generation advanced high strength steels (3G-AHSS). The so-called KS-1B methodology involves pre-straining over-sized tensile specimens followed by the extraction of an ASTM E8 sample, paint baking and re-testing to determine the BHI. Various pre-strain levels in the range of 2 to 10% were considered to evaluate the KS-1B procedure with select comparisons with the ASTM A653 methodology for pre-strain levels of 2 and 8%. Finally, to characterize the influence of paint baking at large strain levels, sheared edge conical hole expansion tests were conducted. The tensile mechanical properties of the 3G steels after paint baking were observed to be sensitive to the pre-strain with bake hardening indices exceeding 100 MPa. However, the sheared edge formability was not significantly affected by paint baking
- Notes:
- Vendor supplied data
- Publisher Number:
- 2025-01-8223
- Access Restriction:
- Restricted for use by site license
The Penn Libraries is committed to describing library materials using current, accurate, and responsible language. If you discover outdated or inaccurate language, please fill out this feedback form to report it and suggest alternative language.