Fatigue of Friction-Stir Welded Joints in Aluminum Tailor Welded Blanks Center for Lightweighting Automotive Materials and Processing University of Michigan-Dearborn

Format:

Conference/Event

Author/Creator:

Raut, A., author.

Conference Name:

SAE 2005 World Congress & Exhibition (2005-04-11 : Detroit, Michigan, United States)

Language:

English

Physical Description:

1 online resource

Place of Publication:

Warrendale, PA SAE International 2005

Summary:

This paper presents the results of fatigue tests conducted on tailor-welded aluminum blanks consisting of 1.66 mm thick and 1.06 mm thick AA 5754-O sheets. The method of joining the sheets was friction-stir welding. The primary purpose of this study was to determine the effect of tensile pre-strains on the fatigue performance of the welded joint. The welded specimens as well as unwelded 1.06-mm thick specimens were subjected to tensile pre-strains of 60 and 80% of their respective uniform strains before the fatigue tests. Fatigue S-N data of all these specimens were compared with similar data for unstrained specimens. Microscopic examinations were conducted to understand the failure modes

Notes:

Vendor supplied data

Publisher Number:

2005-01-1253

Access Restriction:

Restricted for use by site license